Магнитные свойства сплавов Sm2Co17
Марка
|
Br |
Hcb |
Hci |
(BH)max |
Раб. Т.
|
||||
|
T |
kGs |
kA/m |
kOe |
kA/m |
kOe |
kJ/m3 |
MGOe |
°C |
|
|
YXG24 |
0.95 |
9.5 |
640 |
8.0 |
>1350 |
>17 |
160-190 |
20-24 |
250 |
|
YXG26 |
1.05 |
10.5 |
680 |
8.5 |
>1350 |
>17 |
195-215 |
24-26 |
250 |
|
YXG28 |
1.05 |
10.5 |
750 |
9.5 |
>1195 |
>15 |
195-220 |
26-28 |
250 |
|
YXG30 |
1.08 |
10.8 |
780 |
9.8 |
>955 |
>12 |
220-240 |
28-30 |
250 |
Магнитные
свойства сплавов
SmCo5
|
Марка |
Br |
Hcb |
Hci |
(BH)max |
Раб. Т. |
||||
|
T |
kGs |
kA/m |
kOe |
kA/m |
kOe |
kJ/m3 |
MGOe |
°C |
|
|
YX16 |
0. 75-0.88 |
7.5-8.8 |
597± 40 |
7.5± 0.5 |
>1989 |
>25 |
127± 16 |
16± 2 |
250 |
|
YX18 |
0.80-0.93 |
8.0-9.3 |
637± 40 |
8.0±0.5 |
>1432 |
>18 |
143± 16 |
18±2 |
250 |
|
YX20 |
0.85-0.98 |
8.5-9.8 |
637± 40 |
8.0± 0.5 |
>1273 |
>16 |
159±16 |
20±2 |
250 |
|
YXT18 |
0.90-1.03 |
9.0-10.3 |
637± 40 |
8.0± 0.5 |
>1194 |
>15 |
143±16 |
18±2 |
250 |
|
YX22A |
0.90-1.03 |
9.0-10.3 |
653± 40 |
8.2± 0.5 |
>1989 |
>25 |
175± 16 |
22± 2 |
250 |
|
YX22B |
0.90-1.03 |
9.0-10.3 |
635± 40 |
8.2± 0.5 |
>1432 |
>18 |
175±16 |
22± 2 |
250 |
|
YX24 |
0.98-1.08 |
9.8-10.8 |
676± 40 |
8.5± 0.5 |
>1432 |
>18 |
191± 16 |
24± 2 |
250 |
|
YX26A |
1.00-1.13 |
10.0-11.3 |
716± 40 |
9.0± 0.5 |
>1194 |
>15 |
207± 16 |
26±2 |
250 |
|
YX26B |
1.00-1.13 |
10.0-11.3 |
716± 40 |
9.0± 0.5 |
>796 |
>10 |
207± 16 |
26±2 |
250 |
|
YX28 |
1.03-1.13 |
10.3-11.3 |
756± 40 |
9.5± 0.5 |
>1432 |
>18 |
223± 16 |
28± 2 |
250 |
|
YX30 |
1.10-1.20 |
11.0-12.0 |
438-517 |
5.5-6.5 |
454-597 |
5.7-7.5 |
239± 16 |
30± 2 |
250 |
Магнитные свойства сплавов NdFeB
|
Марка |
Br |
Hcb |
Hci
|
(BH)max |
T. рабоч |
||||
|
T |
kGs |
kA/m |
kOe |
kA/m |
kOe |
kJ/m3 |
MGOe |
°C |
|
|
N30 |
1.09-1.14 |
10.9-11.4 |
803.9-867.6 |
10.1-10.9 |
>995.2 |
>12 |
222.8-246.7 |
28-31 |
<80 |
|
N33 |
1.14-1.19 |
11.4-11.9 |
851.7-915.4 |
10.7-11.5 |
>995.2 |
>12 |
246.7-270.6 |
31-34 |
<80 |
|
N35 |
1.18-1.23 |
11.8-12.3 |
867.6-939.2 |
10.9-11.8 |
>995.2 |
>12 |
262.6-286.5 |
33-36 |
<80 |
|
N38 |
1.23-1.28 |
12.3-12.8 |
977.4-971.1 |
11.4-12.2 |
>995.2 |
>12 |
286.5-310.4 |
36-39 |
<80 |
|
N40 |
1.26-1.31 |
12.6-13.1 |
939.2-1002.9 |
11.8-12.6 |
>995.2 |
>12 |
302.4-326.3 |
38-40 |
<80 |
|
N42 |
1.29-1.34 |
12.9-13.4 |
987.0-1026.8 |
12.4-12.9 |
>995.2 |
>12 |
318.4-342.2 |
40-43 |
<80 |
|
N45 |
1.34-1.39 |
13.4-13.9 |
1034.8-1058.6 |
13.0-13.3 |
>995.2 |
>12 |
342.2-366.1 |
43-46 |
<80 |
|
Марка |
Br |
Hcb |
Hci
|
(BH)max |
T. рабоч |
|||||||||||||
|
T |
kGs |
kA/m |
kOe |
kA/m |
kOe |
kJ/m3
MGOe |
MGOe |
°C |
||||||||||
|
|
N33M |
1.15-1.19 |
11.5-11.9 |
876-907 |
11.0-11.4 |
>1114 |
>14 |
183-275 |
32.0-34.5 |
<100 |
||||||||
|
|
N35M |
1.19-1.22 |
11.9-12.2 |
892-923 |
11.2-11.6 |
>1114 |
>14 |
271-291 |
34.0-36.5 |
<100 |
||||||||
|
|
N38M |
1.25-1.28 |
12.5-12.8 |
892-923 |
11.2-11.6 |
>1114 |
>14 |
306-314 |
38.5-39.5 |
<100 |
||||||||
|
|
N40M |
1.28-1.30 |
12.8-13.0 |
876-907 |
11.0-11.4 |
>1114 |
>14 |
309-325 |
38.8-40.8 |
<100 |
||||||||
|
|
N42M |
1.3l-1.33 |
13.l-13.3 |
876-907 |
10.8-11.4 |
>1114 |
>14 |
325-342 |
40.8-43.0 |
<100 |
||||||||
|
|
N45M |
1.33-1.37 |
13.3-13.7 |
860-907 |
10.8-11.4 |
>1114 |
ЎЭ14 |
334-358 |
43.0-45.0 |
<100 |
||||||||
|
Марка |
Br |
Hcb |
Hci |
(BH)max |
T.
рабоч |
||||
|
T |
kGs |
kA/m |
kOe |
kA/m |
kOe |
kJ/m3 |
MGOe |
°C |
|
|
N27H |
1.03-1.08 |
10.3-10.8 |
764.2-827.8 |
9.6-10.4 |
>1353 |
>17 |
199-222.8 |
25-28 |
<120 |
|
N30H |
1.09-1.14 |
10.9-11.4 |
803.9-867.6 |
10.1-10.9 |
>1353 |
>17 |
222.8-246.7 |
28-31 |
<120 |
|
N33H |
1.14-1.19 |
11.4-11.9 |
851.7-915.4 |
10.7-11.5 |
>1353 |
>17 |
246.7-270.6 |
31-34 |
<120 |
|
N35H |
1.18-1.23 |
11.8-12.3 |
867.6-939.2 |
10.9-11.8 |
>1353 |
>17 |
262.6-286.5 |
33-36 |
<120 |
|
N38H |
1.23-1.28 |
12.3-12.8 |
907.4-971.1 |
11.4-12.2 |
>1353 |
>17 |
286.5-310.4 |
36-39 |
<120 |
|
N40H |
1.26-1.31 |
12.6-13.1 |
939.2-1002.9 |
11.8-12.6 |
>1353 |
>17 |
302.4-326.3 |
38-41 |
<120 |
|
N42H |
12.9-13.5 |
1.29-1.35 |
915-1027 |
11.5-12.9 |
>1353 |
>17 |
318-336 |
40-42 |
<120 |
|
Марка |
Br |
Hcb |
Hci |
(BH)max |
T.
рабоч |
||||
|
T |
kGs |
kA/m |
kOe |
kA/m |
kOe |
kJ/m3 |
MGOe |
°C |
|
|
N27SH |
1.03-1.08 |
10.3-10.8 |
764.2-827.8 |
9.6-10.4 |
>1592 |
>20 |
199.0-222.8 |
25-28 |
<150 |
|
N30SH |
1.09-1.14 |
10. 9-11.4 |
803.9-867.6 |
10.1-10.9 |
>1592 |
>20 |
222.8-246.7 |
28-31 |
<150 |
|
N33SH |
1.14-1.19 |
11.4-11.9 |
851.7-915.4 |
10.7-11.5 |
>1592 |
>20 |
246.7-270.6 |
31-34 |
<150 |
|
N35SH |
1.18-1.23 |
11.8-12.3 |
867.6-939.2 |
10.9-11.8 |
>1592 |
>20 |
262.6-286.5 |
33-36 |
<150 |
|
N38SH |
1.22-1.28 |
12.2-12.8 |
907-963 |
11.4-12.1 |
>1592 |
>20 |
287-302 |
36-38 |
<150 |
|
Марка |
Br |
Hcb |
Hci |
(BH)max |
T.
рабоч |
||||
|
T |
kGs |
kA/m |
kOe |
kA/m |
kOe |
kJ/m3 |
MGOe |
°C |
|
|
N28UH |
1.04-1.08 |
10.4-10.8 |
780-812 |
9.8-10.2 |
>1989 |
>24 |
207-223 |
25-28 |
<180 |
|
N30UH |
1.09-1.14 |
10.9-11.4 |
803.9-867.6 |
10.1-10.9 |
>1989 |
>24 |
223-247 |
28-31 |
<180 |
|
N33UH |
1.09-1.14 |
10.9-11.4 |
803.9-867.6 |
10.1-10.9 |
>1989 |
>24 |
251-267 |
31-33 |
<180 |
|
Марка |
Br |
Hcb |
Hci |
(BH)max |
T.
рабоч |
||||
|
T |
kGs |
kA/m |
kOe |
kA/m |
kOe |
kJ/m3 |
MGOe |
°C |
|
|
N27EH |
1.04-1.06 |
10.4-10.6 |
756-828 |
9.5-10.4 |
>2388 |
>30 |
205-219 |
25.8-27.5 |
<200 |
|
N28EH |
1.07-1.09 |
10.7-10.9 |
780-836 |
9.8-10.5 |
>2388 |
>30 |
211-227 |
26.5-28.5 |
<200 |
|
N30EH |
1.09-1.15 |
10.9-11.5 |
796-923 |
10.0-11.2 |
>2388 |
>30 |
227-251 |
28.5-31.5 |
<200 |
|
N16L |
0.77-0.82 |
7.7-8.2 |
573-613 |
7.2-7.7 |
>1353 |
>17 |
111-127 |
14-16 |
<120 |
Температурная стабильность разных классов постоянных магнитов
С
повышением температуры остаточная индукция всех материалов для
постоянных магнитов уменьшаются. Коэрцитивная сила, как правило,
тоже уменьшается, но в случае ферритов –увеличивается.
До
определенной температуры изменение магнитных свойств носит обратимый
характер, т.е. при снижении температуры магнитные свойства
восстанавливаются. Эта температура называется максимальной рабочей
температурой постоянного магнита. При нагревании магнита выше этой
температуры наблюдаются необратимые потери остаточной индукции
магнита, которые могут быть устранены только повторным
намагничиванием постоянного магнита до насыщения.
Максимальная рабочая температура магнита сильно зависит от его
геометрической формы и соотношения размеров. При одинаковом диаметре
цилиндрических магнитов более высокие магниты всегда имеют более
высокую максимальную рабочую температуру. Магниты в форме
прямоугольных параллепипедов всегда на 15-200С
термостабильнее цилиндрических магнитов из того же материала (при
одинаковом отношении
L/D и
A/C). В
таблицах максимальная рабочая температура приводиться для
цилиндрических магнитов с
L/D
=0,7.
Часто бывает важно знать,
насколько уменьшиться остаточная индукция магнита при повышенной
температуре. Поэтому важной характеристикой магнитного материала
является коэфициент обратимых потерь остаточной индукции
α(Br).
Значения этого коэфициента для разных классов магнитов приведены в
таблице
|
|
Феррит |
SmCo5 |
Sm2Co17 |
NdFeB |
Альнико (ЮНДК) |
|
b(НС) |
0.03%/0С |
-0.03%/0С |
-0.3%/0С |
-0.6%/0С |
-0.01%/0С |
|
α(Br) |
-0.20%/0С |
-0.045%/0С |
-0.03%/0С |
-0.10%/0С |
-0.02%/0С |
|
Макс.рабочая температура |
3000С |
2500С |
3000С |
1800С |
5400С |
|
Температура Кюри |
4500С |
7500С |
8250С |
3100С |
810-8600С |
Например,
остаточная индукция термостабильного магнита на основе
NdFeB при нагревании на 1000С выше комнатной уменьшиться на 10% ,
а остаточная индукция
магнита на основе
Sm2Co17
только на 3%.
Следует отметить, что
α(Br) измеряется в замкнутой магнитной цепи. Это означает, что, например,
изменение индукции на поверхности тонких дисков из самарий-кобальта
будет больше, чем значение, рассчитанное с использованием даных
таблицы.
Существуют марки постоянных магнитов с понижеными
коефициентами обратимых потерь остаточной индукции:
YXT 18
(Br=0.9-1.03
Tl,
BНС=8kOe,
IНС=15kOe,
(BH)max=18±2
MGOe) на основе
SmCo.
α(Br) <-0.015%/0С
N16L (Br=0.77-0.82 Tl, BНС=7.2-7.7kOe, IНС=17kOe, (BH)max=15±1 MGOe )
на основе
NdFeB.
α(Br) <-0.01%/0С